Engineering analysis of DLC coated polymeric materials for biomedical applications
Diamond-like carbon (DLC) films have received much attention recently owing to their properties, which are similar to diamond: hardness, thermal conductivity, corrosion resistance against chemicals, abrasion resistance, good biocompatibility, and uniform flat surface. Furthermore, DLC films can be deposited easily on many substrates for wide area coat at room temperature. DLC films were developed for applications as biomedical materials in blood contacting-devices (e.g., rotary blood pump) and showed good biocompatibility for these applications. In this study, we investigated the surface roughness by Atomic Force Microscopy (AFM) and Hi-vision camera, SEM for surface imaging. The DLC films were produced by radio frequency glow discharge plasma decomposed of hydrocarbon gas at room temperature and low pressure (53 Pa) on several kinds of polycarbonate substrates. For the evaluation of the relation between deposition rate and platelet adhesion that we investigated in a previous study, DLC films were deposited at the same methane pressure for several deposition times, and film thickness was investigated. In addition, the deposition rate of DLC films on polymeric substrates is similar to the deposition rate of those deposited on Si substrates. There were no significant differences in substrates' surface roughness that were coated by DLC films in different deposition rates (16–40 nm). The surface energy and the contact angle of the DLC films were investigated. The chemical bond of DLC films also was evaluated. The evaluation of surface properties by many methods and measurements and the relationship between the platelet adhesion and film thickness is discussed. Finally, the presented DLC films appear to be promising candidates for biomedical applications and merit investigation.