Reforming of methane by CO2 over bimetallic Ni-Mn/γ-Al2O3 catalyst
Al-Fatesh, A. H. Fakeeha, M. A. Naeem, W. U. Khan, A. E. Abasaeed, A. S. . 2014
γ-Al2O3 supported Ni-Mn bimetallic catalysts for CO2 reforming of methane were prepared by impregnation method. The reforming reactions were conducted at 500–700 °C and atmospheric pressure using CO2/CH4/N2 with feed ratio of 17/17/2, at total flow rate of 36 mL/min. The catalytic performance was assessed through CH4 and CO2 conversions, synthesis gas ratio (H2/CO) and long term stability. Catalytic activity and stability tests revealed that addition of Mn improved catalytic performance and led to higher stability of bimetallic catalysts which presented better coke suppression than monometallic catalyst. In this work, the optimum loading of Mn which exhibited the most stable performance and least coke deposition was 0.5wt%. The fresh and spent catalysts were characterized by various techniques such as Brunauer-Emmett-Teller, the temperature programmed desorption CO2-TPD, thermogravimetric analysis, X-ray diffraction, scanning electron microscope, EDX, and infrared spectroscopy
20% iron catalysts supported on combined alumina and silica through different proportions (Al2O3:SiO2:
100:0.00, 90.0:10.0, 80.0:20.0 and 0.0:100.0) were tested for the catalytic…
A novel approach to the in situ regeneration of a spent alumina-supported cobalt–iron
catalyst for catalytic methane decomposition is reported in this work. The spent catalyst was
…