Suppression of carbon formation in CH4–CO2 reforming by addition of Sr into bimetallic Ni–Co/γAl2O3 catalyst
Al-Fatesh, A. S. . 2015
Bimetallic catalysts, containing 5 wt% Ni + 5 wt% Co supported on γ-Al2O3 combined with different amounts of Sr promoter ranging from 0 to 1 wt%, for dry reforming reaction were prepared by the impregnation method. The dry reforming reaction was carried out at atmospheric pressure using CO2/CH4/N2 feed ratio of 17/17/2, F/W = 60 mL/min gcat and reaction temperature range of 500–700 °C. The performance of the developed catalyst was evaluated by estimating the CH4 and CO2 conversions, and by performing a long run stability test. The fresh and spent catalysts were characterized by BET, TGA, TPD, TPR, and TPO. The bimetallic catalysts provided higher activity than the monometallic-catalysts. When the bimetallic was promoted with Sr, the activity decreased slightly however, the stability enhanced. The best stability, estimated by the deactivation factor, and less carbon deposition, measured by TGA, were obtained when 5Ni5CoSr0.75 catalyst was used
20% iron catalysts supported on combined alumina and silica through different proportions (Al2O3:SiO2:
100:0.00, 90.0:10.0, 80.0:20.0 and 0.0:100.0) were tested for the catalytic…
A novel approach to the in situ regeneration of a spent alumina-supported cobalt–iron
catalyst for catalytic methane decomposition is reported in this work. The spent catalyst was
…