Comparative Study on Electronic, Emission, Spontanous Property of Porous Silicon in Different Solvent
, M. Naziruddin Khan . 2014
Luminescent porous silicon (Psi) fabricated by simple chemical etching technique in different organic solvents was studied. By quantifying the silicon wafer piece, optical properties of the Psi in solutions were investigated. Observation shows that no photoluminescence light of Psi in all solvents is emitted. Morphology of Psi in different solvents indicates that the structure and distribution of Psi are differently observed. Particles are uniformly dispersive with the sizes around more or less 5–8 nm. The crystallographic plane and high crystalline nature of Psi is observed by selected area diffraction (SED) and XRD. Electronic properties of Psi in solutions are influenced due to the variation of quantity of wafer and nature of solvent. Influence in band gaps of Psi calculated by Tauc’s method is obtained due to change of absorption edge of Psi in solvents. PL intensities are observed to be depending on quantity of silicon wafer, etched cross-section area on wafer surface. Effects on emission peaks and bands of Psi under temperature annealing are observed. The spontaneous signals of Psi measured under high power Pico second laser 355 nm source are significant, influenced by the nature of solvent, pumped energy, and quantity of Si wafer piece used in etching process.
In this study, we investigated the optoelectronic properties of cubic (Pm3m) and orthorhombic (Pnma) CsPbX3 (X = I, Br, and Cl). We utilized the full potential linear augmented plane wave method,…
The goal of this research is to see how excitation wavelength affects steady-state photoluminescence (PL), time-resolved photoluminescence (TRPL), and amplified spontaneous emission (ASE) in…
A solid redox mediator (solid electrolyte) with an electrical conductivity (σ25°C) greater than 10−4 S cm−1 is an essential requirement for a dye-sensitized solar cell in the harsh weather of Gulf…